Low emissivity film for high temperature processing

ABSTRACT

A multiple-layer, high transmittance, low emissivity coated article which can be subjected to high temperature processing such as bending, annealing, tempering, laminating or glass welding as a result of primer layers comprising metal and metal oxide is disclosed.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of U.S. Ser. No. 947,799 filed Dec. 29, 1986, U.S. Pat. No. 4,806,220, by the same inventor and is related in subject matter to U.S. Ser. No. 176,979 filed Apr. 4, 1989, by the same inventor.

BACKGROUND OF THE INVENTION

The present invention relates generally to the art of cathode sputtering of metal oxide films, and more particularly to the art of magnetic sputtering of multiple layer films of metal and metal oxide.

U.S. Pat. No. 4,094,763 to Gillery et al discloses producing transparent, electroconductive articles by cathode sputtering metals such as tin and indium onto refractory substrates such as glass at a temperature above 400° F. in a low pressure atmosphere containing a controlled amount of oxygen.

U.S. Pat. No. 4,113,599 to Gillery teaches a cathode sputtering technique for the reactive deposition of indium oxide in which the flow rate of oxygen is adjusted to maintain a constant discharge current while the flow rate of argon is adjusted to maintain a constant pressure in the sputtering chamber.

U.S. Pat. No. 4,166,018 to Chapin describes a sputtering apparatus in which a magnetic field is formed adjacent a planar sputtering surface, the field comprising arching lines of flux over a closed loop erosion region on the sputtering surface.

U.S. Pat. No. 4,201,649 to Gillery discloses a method for making low resistance indium oxide thin films by first depositing a very thin primer layer of indium oxide at low temperature before heating the substrate to deposit the major thickness of the conductive layer of indium oxide by cathode sputtering at typically high cathode sputtering temperatures.

U.S. Pat. No. 4,327,967 to Groth discloses a heat-reflecting panel having a neutral-color outer appearance comprising a glass pane, an interference film having a refractive index greater than 2 on the glass surface, a heat reflecting gold film over the interference film and a neutralization film of chromium, iron, nickel, titanium or alloys thereof over the gold film.

U.S. Pat. No. 4,349,425 to Miyake et al discloses d-c reactive sputtering of cadmium-tin alloys in argon-oxygen mixtures to form cadmium-tin oxide films having low electrical resistivity and high optical transparency.

U.S. Pat. No. 4,462,883 to Hart discloses a low emissivity coating produced by cathode sputtering a layer of silver, a small amount of metal other than silver, and an antireflection layer of metal oxide onto a transparent substrate such as glass. The antireflection layer may be tin oxide, titanium oxide, zinc oxide, indium oxide, bismuth oxide or zirconium oxide.

In the interest of improving the energy efficiency of double-glazed window units, it is desirable to provide a coating on one of the glass surfaces which increases the insulating capability of the unit by reducing radiative heat transfer. The coating therefore must have a low emissivity in the infrared wavelength range of the radiation spectrum. For practical reasons, the coating must have a high transmittance in the visible wavelength range. For aesthetic reasons, the coating should have a low luminous reflectance and preferably be essentially colorless.

High transmittance, low emissivity coatings as described above generally comprise a thin metallic layer, for infrared reflectance and low missivity, sandwiched between dielectric layers of metal oxides to reduce the visible reflectance. These multiple layer films are typically produced by cathode sputtering, especially magnetron sputtering. The metallic layer may be gold or copper, but is generally silver. The metal oxide layers described in the prior art include tin oxide, indium oxide, titanium oxide, bismuth oxide, zinc oxide, zirconium oxide and lead oxide. In some cases, these oxides incorporate small amounts of other metals, such as manganese in bismuth oxide, indium in tin oxide and vice verse, to overcome certain disadvantages such as poor durability or marginal emissivity. However, all of these metal oxides have some deficiency.

Although the coating may be maintained on an interior surface of a double-glazed window unit in use, where it is protected from the elements and environmental agents which would cause its deterioration, a durable effective coating able to withstand handling, packaging, washing and other fabrication processes encountered between manufacture and installation is particularly desirable. These properties are sought in the metal oxide. However, in addition to hardness which provides mechanical durability, inertness which provides chemical durability, and good adhesion to both the glass and the metal layer, the metal oxide should have the following properties as well.

The metal oxide must have a reasonably high refractive index, preferably greater than 2.0, to reduce the reflection of the metallic layer and thus enhance the transmittance of the coated product. The metal oxide must also have minimal absorption to maximize the transmittance of the coated product. For commercial reasons, the metal oxide should be reasonably priced, have a relatively fast deposition rate by magnetron sputtering, and be nontoxic.

Perhaps the most important, and most difficult to satisfy, requirements of the metal oxide film relate to its interaction with the metallic film. The metal oxide film must have low porosity, to protect the underlying metallic film from external agents, and low diffusivity for the metal to maintain the integrity of the separate layers. Finally, and above all, the metal oxide must provide a good nucleation surface for the deposition of the metallic layer, so that a continuous metallic film can be deposited with minimum resistance and maximum transmittance. The characteristics of continuous and discontinuous silver films are described in U.S. Pat. No. 4,462,884 to Gillery et al the disclosure of which is incorporated herein by reference.

Of the metal oxide multiple-layer films in general use, those comprising zinc oxide and bismuth oxide are insufficiently durable, those oxides being soluble in both acid and alkaline agents, with the multiple-layer film being degraded by fingerprints, and destroyed in salt, sulfur dioxide and humidity tests. Indium oxide, preferably doped with tin, is more durable and protective of an underlying metal layer; however, indium sputters slowly and is relatively expensive. Tin oxide, which may be doped with indium or antimony, is also more durable and protective of an underlying metal layer, but does not provide a suitable surface for nucleation of the silver film, resulting in high resistance and low transmittance. The characteristics of a metal oxide film which result in proper nucleation of a subsequently deposited silver film have not been established; however, trial-and-error experimentation has been widely practiced with the metal oxides described above.

U.S. Pat. No. 4,610,771 to Gillery, the disclosure of which is incorporated herein by reference, provides a novel film composition of an oxide of a zinc-tin alloy, as well as a novel multiple-layer film of silver and zinc-tin alloy oxide layers for use as a high transmittance, low emissivity coating.

U.S. Pat. No. 4,716,086 to Gillery discloses improving the durability of multiply layer films, especially multiple layer films comprising antireflective metal and/or metal alloy oxide layers and infrared reflective metal layers such as silver, by providing an exterior protective layer of a particularly chemical resistant material such as titanium oxide.

U.S. application Ser. No. 841,056 filed Mar. 17, 1986, by Gillery et al discloses improving the durability of multiple layer films, especially multiply layer films comprising antireflective metal and/or metal alloy oxide layers and infrared reflective metal layers such as silver, by providing a primer layer such as copper which improves adhesion between the metal and metal oxide layers.

While multiple-layer, low-emissivity, high transmittance films have been made sufficiently durable for architectural applications in multiple glazed window units, such films have not been sufficiently temperature-resistant to withstand high temperature processing, such as tempering or bending.

SUMMARY OF THE INVENTION

The present invention involves a novel multiple-layer coating which is sufficiently temperature resistant to enable coated substrates such as glass to be subjected to high temperature processing such as bending, annealing, tempering, laminating or glass welding. The novel multiple-layer coating of the present invention comprises a first antireflective metal oxide layer such as an oxide of zinc and tin, an infrared reflective metal layer such as silver, a primer layer of titanium metal and titanium oxide, a second antireflective metal oxide layer and, preferably, an exterior protective layer of titanium metal or titanium oxide.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A film composition preferably comprising an oxide of a metal or metal alloy is preferably deposited by cathode sputtering, preferably magnetron sputtering. A cathode target is prepared comprising the desired metal or metal alloy elements. The target is then sputtered in a reactive atmosphere, preferably containing oxygen in order to deposit a metal or metal alloy oxide film on a surface of a substrate.

A preferred metal alloy oxide in accordance with the present invention is an oxide of an alloy comprising zinc and tin. A zinc/tin alloy oxide film may be deposited in accordance with the present invention by cathode sputtering, preferably magnetically enhanced. Cathode sputtering is also a preferred method for depositing high transmittance, low emissivity films in accordance with the present invention. Such films typically comprise multiple layers, preferably a layer of a highly reflective metal such as gold or silver sandwiched between antireflective metal oxide layers such as indium oxide or titanium oxide, or preferably an oxide of an alloy of zinc and tin which preferably comprises zinc stannate.

While various metal alloys may be sputtered to form metal alloy oxide films, in order to produce a preferred high transmittance, low emissivity multiple layer film in accordance with the present invention, alloys of tin and zinc are preferred. A particularly preferred alloy comprises zinc and tin, preferably in proportions of 10 to 90 percent zinc and 90 to 10 percent tin. A preferred zinc/tin alloy ranges from 30 to 60 percent zinc, preferably having a zinc/tin ratio from 40:60 to 60:40. A most preferred range is 46:54 to 50:50 by weight tin to zinc. A cathode of zinc/tin alloy reactively sputtered in an oxidizing atmosphere results in the deposition of a metal oxide layer comprising zinc, tin and oxygen, preferably comprising zinc stannate, Zn₂ SnO₄. Such a metal alloy oxide layer may also be deposited by simultaneously sputtering zinc and tin in suitable proportions. However, it is more convenient to use a metal alloy target.

In a conventional magnetron sputtering process, a substrate is placed within a coating chamber in facing relation with a cathode having a target surface of the material to be sputtered. Preferred substrates in accordance with the present invention include glass, ceramics and plastics which are not detrimentally affected by the operating conditions of the coating process.

The cathode may be of any conventional design, preferably an elongated rectangular design, connected with a source of electrical potential, and preferably employed in combination with a magnetic field to enhance the sputtering process. At least one cathode target surface comprises a metal alloy such as zinc/tin which is sputtered in a reactive atmosphere to form a metal alloy oxide film. The anode is preferably a symmetrically designed and positioned assembly as taught in U.S. Pat. No. 4,478,702 to Gillery et al, the disclosure of which is incorporated herein by reference.

In a preferred embodiment of the present invention, a multiple layer film is deposited by cathode sputtering to form a high transmittance, low emissivity coating. In addition to the metal alloy target, at least one other cathode target surface comprises a metal to be sputtered to form a reflective metallic layer. At least one additional cathode target surface comprises the titanium to be sputtered to deposit a titanium oxide layer. A durable multiple layer coating having a reflective metallic film in combination with an antireflective metal alloy oxide film is produced as follows, using a titanium oxide primer layer to improve the adhesion between the metal and metal oxide films, which primer layer also provides high-temperature resistance to the multiple-layer coating in accordance with the present invention so that the resultant coated article may be subjected to high temperature processing, such as bending, annealing, tempering, laminating, or glass welding without deterioration of the coating.

While primer layers of the prior art are preferably of minimal thickness, the thickness of the primer layer of the present invention is preferably between 10 and 100 Angstroms, most preferably 12 to 30 Angstroms. If a single primer layer is deposited over the reflective metal film, the thickness is preferably between 20 and 100 Angstroms. If the thickness of the primer layer over the reflective metal layer is less than 20 Angstroms, preferably an additional primer layer at least 10 Angstroms thick is deposited between the first antireflective metal oxide layer and the reflective metal layer, and the total thickness of the two layers is preferably not more than 100 Angstroms. Although the primer of the present invention may be deposited as titanium metal, it is necessary for the primer layer to be essentially completely oxidized to titanium oxide in the final product. While such oxidation can be readily accomplished by heating for primer layers less than about 50 Angstroms thick, the present invention provides for thicker primer layers wherein the presence of titanium oxide enhances the oxidation of metallic titanium allowing thicker primer layers to be employed without compromising optical properties in the multilayer coated product. For a primer layer under silver, for example, it is preferred to deposit titanium oxide first and then titanium, while for a primer on top of silver it is preferred to deposit titanium first and then titanium oxide. The presence of titanium oxide is more critical in a primer layer under silver, but in either location, it is preferred to have titanium metal in contact with silver in the film as deposited. Upon heating, such as during bending or lamination, the titanium oxidizes to titanium oxide and the transmittance increases.

A multiple-layer low emissivity film is formed on a glass substrate as follows. A clean glass substrate is placed in a coating chamber which is evacuated, preferably to less than 10⁻⁴ torr, more preferably less than 2×10⁻⁵ torr. A selected atmosphere of inert and reactive gases, preferably argon and oxygen, is established in the chamber to a pressure between about 5×10⁻⁴ and 10⁻² torr. A cathode having a target surface of zinc/tin metal is operated over the surface of the substrate to be coated. The target metal is sputtered, reacting with the atmosphere in the chamber to deposit a zinc/tin alloy oxide coating layer on the glass surface.

After the initial layer of zinc/tin alloy oxide is deposited, the coating chamber is evacuated, and an inert atmosphere such as pure argon is established at a pressure between about 5×10⁻⁴ and 10⁻² torr. Preferably, a cathode having a target surface of titanium is first sputtered in an oxidizing atmosphere to deposit titanium oxide and then sputtered in an inert atmosphere to deposit titanium in the primer layer as well. A cathode having a target surface of silver is then sputtered to deposit a reflective layer of metallic silver over the titanium-containing primer layer. A second titanium-containing primer layer is preferably deposited by sputtering titanium over the reflective silver layer. Preferably, the titanium is sputtered in an inert atmosphere to deposit a titanium metal primer layer. Finally, a second layer of zinc/tin alloy oxide is deposited over the second titanium primer layer under essentially the same conditions used to deposit the first zinc/tin alloy oxide layer. The second primer layer may comprise titanium oxide as well as titanium metal, so long as titanium is sputtered in an inert atmosphere over the silver first.

In most preferred embodiments of the present invention, a protective overcoat is deposited over the final metal oxide film. The protective overcoat is preferably deposited by sputtering over the metal oxide film a layer of a metal such as disclosed in U.S. Pat. No. 4,594,137 to Gillery et al. Preferred metals for the protective overcoat include alloys of iron or nickel, such as stainless steel or Inconel. Titanium is a most preferred overcoat because of its high transmittance. In an alternative embodiment, the protective layer may be a particularly chemical resistant material such as titanium oxide as disclosed in U.S. Pat. No. 4,716,086 to Gillery et al, the disclosure of which is incorporate herein by reference.

The chemical resistance of a multiple layer film is most improved by depositing a protective coating comprising titanium oxide over the multiple layer film. Preferably, the titanium oxide protective coating is deposited by cathode sputtering at a relatively high deposition rate and low pressure, preferably about 3 millitorr. A protective coating comprising titanium oxide may be formed by sputtering titanium in an oxygen-sufficient atmosphere to deposit titanium oxide directly. In an alternative embodiment of the present invention, a protective coating comprising titanium oxide may be formed by sputtering titanium in an inert atmosphere to deposit a titanium-containing film which subsequently oxidizes to titanium oxide upon exposure to an oxidizing atmosphere such as air.

The present invention will be further understood from the description of a specific example which follows. In the example, the zinc/tin alloy oxide film is referred to as zinc stannate although the film composition need not be precisely Zn₂ SnO₄.

EXAMPLE

A multiple layer film is deposited on a soda-lime silica glass substrate to produce a high transmittance, low emissivity coated product. A stationary cathode measuring 5 by 17 inches (12.7 by 43.2 centimeters) comprises a sputtering surface of zinc/tin alloy consisting of 52.4 weight percent zinc and 47.6 percent tin. A soda-lime-silica glass substrate is placed in the coating chamber which is evaluated to establish a pressure of 4 millitorr in an atmosphere of 50/50 argon/oxygen. The cathode is sputtered in a magnetic field at a power of 1.7 kilowatts while the glass is conveyed past the sputtering surface at a rate of 120 inches (3.0 meters) per minute. A film of zinc stannate is deposited on the glass surface. Three passes produce a film thickness of about 300 Angstroms, resulting in a decrease in transmittance from 90 percent for the glass substrate to 84 percent for the zinc stannate coated glass substrate. A stationary cathode with a titanium target is first sputtered in an oxidizing atmosphere to deposit 30 Angstroms of titanium oxide which reduces the transmittance to 82 percent, and is then sputtered in an inert atmosphere to deposit 15 Angstroms of titanium, reducing the transmittance to 72.5 percent. Next, a layer of silver is deposited over the titanium-containing primer layer by sputtering a silver cathode target in an atmosphere of argon gas at a pressure of 4 millitorr. With the substrate passing under the silver cathode target at the same rate, silver is deposited to a film thickness of about 100 Angstroms, further reducing the transmittance to 60 percent. A second 15 Angstrom titanium primer layer is sputtered over the silver layer, decreasing the transmittance to a low of 51.5 percent. Then the second antireflective layer of zinc stannate is deposited to a thickness of 300 Angstroms, increasing the transmittance to 81 percent.

Optionally, a titanium cathode is sputtered at 10 kilowatts in an atmosphere comprising equal volumes of argon and oxygen at a pressure of 3 millitorr to deposit a protective coating of titanium oxide about 15 to 20 Angstroms thick. The protective coating of titanium oxide does not significantly affect the resistance and reflectance properties of the multiple-layer coating, and changes the transmittance no more than about one percent.

The improved durability of the coated article resulting from the improved adhesion between the metal and metal oxide films as a result of the titanium oxide primer layers of the present invention is readily demonstrated by a simple abrasion test consisting of wiping the coated surface with a damp cloth. A surface coated with zinc stannate/silver/zinc stannate having no primer layers increases in reflectance from about 6 percent to about 18 percent after several passes of a damp cloth, indicating removal of both the top zinc stannate and the underlying silver films. In contrast, prolonged vigorous rubbing with a damp cloth produces no visible change in a zinc stannate/titanium oxide-titanium/silver/titaniums/zinc stannate coated article comprising the primer layers of the present invention.

Preferred titanium oxide protective coatings have thicknesses in the range of about 10 to 50 Angstroms. Thicker titanium oxide coatings may be used, limited only by the desired transmittance of the article. With a titanium oxide protective coating about 20 Angstroms thick, the durability of a multiple layer coating in accordance with this example is increased from 2 hours to 22 hours in a 21/2 percent salt solution at ambient temperature, and from 5 hours to one week in the Cleveland humidity test conducted with a Q-Panel Cleveland Condensation Tester Model QCT-ADO containing deionized water at 150° F. (about 66° C.).

The above example is offered to illustrate the present invention. Various modifications of the product and the process involving titanium/titanium oxide primers are included, such as varying their relative and absolute thickness, and may be carried out in such a primer at any location in a multilayer coating. The use of such a metal/metal oxide primer may also be practiced using zirconium. Other coating compositions are within the scope of the present invention, particularly other antireflective metal oxides and infrared reflective metals such as gold or copper. Depending on the proportions of zinc and tin when a zinc/tin oxide film is deposited, the coating may contain widely varying amounts of zinc oxide and tin oxide in addition to zinc stannate. The thicknesses of the various layers are limited primarily by the desired optical properties such as transmittance. Process parameters such as pressure and concentration of gases may be varied over a broad range. Protective coatings of other chemically resistant materials may be deposited as either metal or oxides. The scope of the present invention is defined by the following claims. 

I claim:
 1. A high transmittance, low emissivity article comprising:a. a transparent nonmetallic substrate; b. a first transparent antireflective metal oxide film deposited on a surface of said substrate; c. a transparent infrared reflective metallic film; d. a transparent metal-containing primer film deposited on said infrared reflective metallic film comprising a first layer of metal and a second layer of metal oxide; and e. a second transparent antireflective metal oxide film deposited on said primer film wherein said primer film comprises a different metal oxide from said second antireflective metal oxide film.
 2. An article according to claim 1, wherein the substrate is glass.
 3. An article according to claim 2, wherein the infrared reflective metallic film is silver.
 4. An article according to claim 3, wherein the metal oxide comprises an oxide reaction product of zinc and tin.
 5. An article according to claim 1, wherein said metal-containing primer film comprises a metal selected from the group consisting of titanium and zirconium.
 6. An article according to claim 5, wherein the metal-containing primer film comprises titanium.
 7. An article according to claim 1, further comprising a protective metal-containing overcoat deposited over said second antireflective metal oxide film.
 8. An article according to claim 1, further comprising an additional transparent metal-containing primer film deposited on said first transparent antireflective metal oxide film.
 9. An article according to claim 8, wherein said additional primer film comprises a first layer of metal oxide and a second layer of metal onto which said infrared reflective metallic film is deposited.
 10. An article according to claim 9, wherein the metal of said primer film is selected from the group consisting of titanium and zirconium.
 11. An article according to claim 10, wherein the metal is titanium.
 12. An article according to claim 11, wherein the primer film deposited on said infrared reflective metallic film comprises titanium. 